• 专利标题:   Preparation of graphene oxide-polyethyleneimine/silica composite aerogel involves stripping graphene oxide aqueous solution, mixing with polyethyleneimine, heat-preserving, adding to silica precursor solution, condensing, and freeze-drying.
  • 专利号:   CN113477236-A
  • 发明人:   YU J, LEI C, LIU Y, HE J, DU Y, SONG M
  • 专利权人:   NORTHWEST INST NONFERROUS METALS
  • 国际专利分类:   B01J020/30, B01D053/04, B01J020/28, B01J020/26
  • 专利详细信息:   CN113477236-A 08 Oct 2021 B01J-020/26 202103 Chinese
  • 申请详细信息:   CN113477236-A CN10972127 24 Aug 2021
  • 优先权号:   CN10972127

▎ 摘  要

NOVELTY - Preparation of graphene oxide-polyethyleneimine/silica composite aerogel comprises stripping graphene oxide aqueous solution through an ultrasonic water bath to obtain a uniformly dispersed graphene oxide dispersion and adjusting pH value with sodium hydroxide aqueous solution; mixing the graphene oxide dispersion liquid after adjusting the pH value with polyethyleneimine aqueous solution to prepare a graphene oxide-polyethyleneimine mixed liquid; putting into a mold, heat-preserving, removing the film, and soaking in deionized water to obtain a graphene oxide-polyethyleneimine hydrogel; preparing silica precursor solution, adding hydrogel, immersing, and condensing under low temperature; and subjecting to solution replacement and freeze-drying. USE - The method is used for preparing graphene oxide-polyethyleneimine/silica composite aerogel. ADVANTAGE - The method improves amine functional group loading amount, avoids sensitive crushing phenomenon of the silicon dioxide gel, and improves the adsorption performance of the composite aerogel.