▎ 摘　　要

NOVELTY - Water-proof and moisture-proof processing of bamboo-wood fibre door plate involves weighing 8-10 pts. wt. bamboo fibre, 2-3 pts. wt. magnesium oxide, 3-4 pts. wt. magnesium chloride, 5-7 pts. wt. industrial salt, 7-9 pts. wt. rubber powder, 6-7 pts. wt. lime and 4-5 pts. wt. fermenting agent, firstly processing the waste of bamboo and wood processing factory into 8-10 pts. wt. bamboo fibre, then grinding 2-3 pts. wt. magnesium oxide, 3-4 pts. wt. magnesium chloride, 5-7 pts. wt. industrial salt, 7-9 pts. wt. rubber powder and 6-7 pts. wt. quicklime to the diameter between 110-120 meshes of powder, sending the air or oxygen-enriched air to the furnace after reaching a certain temperature in the heating furnace, then putting 2-3 pts. wt. grounded magnesium oxide, 3-4 pts. wt. magnesium chloride, 5-7 pts. wt. industrial salt, 7-9 pts. wt. rubber powder and 6-7 pts. wt. quicklime powder to the heating furnace. USE - Water-proof and moisture-proof processing of bamboo-wood fibre door plate used in bamboo fiber board technology field and in construction industry. ADVANTAGE - The method enables to process bamboo fiber door plate, which is an electrolytic layer/electrostatic layer harmless to the human body through the chemical film on the bamboo fibre door plate and realizes the waterproof and moisture-proof effect, but also realizing electrostatic dust-proof effects. DETAILED DESCRIPTION - Water-proof and moisture-proof processing of bamboo-wood fibre door plate involves weighing 8-10 pts. wt. bamboo fibre, 2-3 pts. wt. magnesium oxide, 3-4 pts. wt. magnesium chloride, 5-7 pts. wt. industrial salt, 7-9 pts. wt. rubber powder, 6-7 pts. wt. lime and 4-5 pts. wt. fermenting agent, firstly processing the waste of bamboo and wood processing factory into 8-10 pts. wt. bamboo fibre, then grinding 2-3 pts. wt. magnesium oxide, 3-4 pts. wt. magnesium chloride, 5-7 pts. wt. industrial salt, 7-9 pts. wt. rubber powder and 6-7 pts. wt. quicklime to the diameter between 110-120 meshes of powder, sending the air or oxygen-enriched air to the furnace after reaching a certain temperature in the heating furnace, then putting 2-3 pts. wt. grounded magnesium oxide, 3-4 pts. wt. magnesium chloride, 5-7 pts. wt. industrial salt, 7-9 pts. wt. rubber powder and 6-7 pts. wt. quicklime powder to the heating furnace, then starting the motor to stir the material, until the raw material is changed into solution, adding 4-5 pts. wt. fermenting agent into the solution, continuously starting the motor stirring until the solution becomes the first gel slurry. The bamboo fibre plate blank obtained is immersed in the first gel slurry prepared for 8-15 minutes, the material is reserved, taken out the plate blank soaked into the roller pressing machine to roll, then placed the rolled plate into a dryer for drying, reduced the water content of the structure plate, left the material, finally cut the plate obtained, pressed and covered film to obtain the gelled structure plate finished product, obtained the bamboo-wood fibre plate, the dendritic polyamide-6 formic acid solution prepared by the electrostatic spinning technology is added to form the second gel slurry, formed a spinning fibre film layer on the plate blank, placed the dried structure plate into the high voltage electrostatic field, the spinning voltage of the spinning fibre film layer is 1-5V to form the electrolyte film on the outer surface of the bamboo-wood fibre plate, placed the plate into the dryer, coating lithium battery anode material powder raw material to the outer surface of the plate blank according to proportion and dried graphene modified cathode material powder raw material.