▎ 摘　　要

NOVELTY - Manufacture of natural graphite composite material involves mixing coal-based powder having median diameter of 5-10 mu m, and natural graphite having median diameter of 6-10 mu m, in weight ratio of 100:30-100, adding asphalt micropowder having maximum particle size of 2 mu m or less to the mixture in weight ratio of 100:30-100, modifying at 300-600 degrees C, graphitizing at 2800-3200 degrees C, adding graphene to the mixture in weight ratio of 100:30-80, carbonizing at 1200-1500 degrees C, cooling to room temperature, pulverizing, and sieving. USE - Manufacture of natural graphite composite material (claimed). ADVANTAGE - The method enables efficient manufacture of natural graphite composite material with excellent high/low-temperature performance, processing performance, conductivity and productivity.