▎ 摘　　要

NOVELTY - Preparing amorphous ternary transition metal sulfide/graphene composite material involves adding stannous chloride dihydrate, transition metal salt, and thioacetamide to the graphene oxide dispersion, mixing well, and placing them in a water bath at 50-100 degrees C after the reaction, cooling to room temperature after washing with water and ethanol to obtain amorphous ternary transition metal sulfide/graphene composite was obtained after drying, where ratio of stannous chloride dihydrate to graphene oxide is 0.5-5: 30-90 mmol: mg, and ratio of stannous chloride dihydrate to transition metal salt is 1-5: 2-10. USE - Method for preparing amorphous ternary transition metal sulfide/graphene composite material. ADVANTAGE - The method enables to prepare amorphous ternary transition metal sulfide/graphene composite material does not require high-temperature calcination, and can prepare amorphous, non-agglomerated, and high-purity powder materials, has low energy consumption, and in simple manner.