• 专利标题:   Composition for preparing carrier roller body, comprises polyvinyl chloride, ultra-high molecular weight polyethylene, stabilizer, modifier, lubricant, composite antistatic agent, where stabilizer is chlorinated polyethylene or composite lead salt heat stabilizer.
  • 专利号:   CN114381058-A
  • 发明人:   WANG X, SUN L, LI Y, FU W, DING L, BAI R, WANG Z, YUAN Y
  • 专利权人:   SHANDONG HUASIDA IND TRADE CO LTD, SHENHUA TECHNOLOGY DEV CO LTD
  • 国际专利分类:   C08K003/04, C08K003/30, C08K005/09, C08K005/098, C08K007/26, C08L023/06, C08L023/28, C08L027/06, C08L051/04, C08L055/02, C08L077/00, C08L091/06
  • 专利详细信息:   CN114381058-A 22 Apr 2022 C08L-023/06 202274 Chinese
  • 申请详细信息:   CN114381058-A CN11442959 30 Nov 2021
  • 优先权号:   CN11442959

▎ 摘  要

NOVELTY - Composition comprises 1-65 pts. wt., preferably 5-50 pts. wt. polyvinyl chloride, 1-55 pts. wt., preferably 20-45 pts. wt. ultra-high molecular weight polyethylene, 1-20 pts. wt., preferably 10-15 pts. wt. stabilizer, 3-45 pts. wt., preferably 10-30 pts. wt. modifier, 2-10 pts. wt., preferably 3-5 pts. wt. lubricant, 0-15 pts. wt., preferably 3-9 pts. wt. composite antistatic agent. The stabilizer is chlorinated polyethylene or composite lead salt heat stabilizer. The modifier is Methyl Methacrylate Butadiene Styrene polymer (MBS), polyamide (PA), stearic acid, lead stearate, microbead filler or acrylonitrile butadiene styrene (ABS) resin. The lubricant is paraffin or molybdenum disulfide. The composite antistatic agent comprises polyvinyl chloride (PVC) antistatic agent, carbon black and graphene. USE - Composition for preparing carrier roller body, preferably ceramic carrier roller used in carrier roller bearing seat of a vehicle. ADVANTAGE - The composition has excellent flame-retardant, antistatic and wear-resistant ability. DETAILED DESCRIPTION - INDEPENDENT CLAIMS are included for: Method for preparing composition, which involves mixing polyvinyl chloride, ultrahigh molecular weight polyethylene, stabilizer, modifier and lubricant to obtain first mixture; and mixing the first mixture with a composite antistatic agent to obtain composition. Method for preparing carrier roller body using composition, which involves: (1) granulating the composition to obtain composition particles; and (2) extruding and molding the composition particles to obtain the carrier roller body.