▎ 摘　　要

NOVELTY - Graphene pickering emulsion comprises 1-20 pts. wt. modified graphene, 10-50 pts. wt. oil phase liquid and 10-40 pts. wt. aqueous-phase liquid. USE - Used as graphene pickering emulsion. ADVANTAGE - The composition wetness, low rolling resistance and low heating performance increased by more than 10%, emulsion effectively stabilizes the particle diameter of the white carbon black to achieve more uniformly dispersed, so that moisture and low heating performance increased and caused hysteresis of viscoelastic (hysteresis) and helping improve the low rolling resistance reduced. DETAILED DESCRIPTION - INDEPENDENT CLAIMS are also included for: (1) preparing graphene pickering emulsion, comprising weighing oil phase liquid and pouring into a container, then adding weighed aqueous-phase liquid, and then adding modified graphene dispersing for 0-1 hour and ultrasonic oscillating for 0-2 hours by table concentrator instrument swing; (2) graphene piclin emulsion optimized rubber composition comprising 100 pts. wt. crude rubber, 20-90 pts. wt. filling material, 1-20 pts. wt. modified graphite 10-50 pts. wt. oil phase liquid, 10-40 pts. wt aqueous-phase liquid and 1.6-7.2 pts. wt. silane coupling agent; and (3) preparing the composition, comprising using first stage mixer, conditions as initial temperature is 20-90 degrees C, rotating speed is 30-80 rotations/minute, pressure is 0.2-0.8 MPa, the feeding order is first action, into rubber mixing for 10-60 seconds, the second action, adding 1/2 filling material and mixing for 10-60 seconds, the third action, adding 1/2 filling material, silane coupling agent and graphene pickering emulsion for 10-60 seconds, fourth action, cleaning, the fifth action, cleaning, the sixth action, discharging (one day), the second stage mixer is used, the condition is initial temperature is 20-90 degrees C, rotating speed is 30-80 rotations/minute, the pressure is 0.2-0.8 MPa, the feeding order is first action, the upper space sizing material mixing for 10-60 seconds, the second action, adding plasticizer, anti-aging agent, protective wax, stearic acid and nano-zinc oxide and mixing for 10-60 seconds, the third action, cleaning, a fourth action, cleaning, the fifth action, discharging (one day), the third stage mixer is used, conditions as initial temperature is 20-60 degrees C, rotating speed is 30-80 rotations/minute, pressure is 0.2-0.8 MPa, the feeding order is first action, the upper space rubber material continuously mixing for 10 to 60 seconds, the second action, adding sulfur and accelerator, the third action, cleaning, a fourth action, cleaning, the fifth action, discharging.