• 专利标题:   Preparation of nanometer ferroferric oxide loaded graphene composite for e.g. electromagnetic material involves preparing mixed stock solution of sodium hydroxide and diethylene glycol, and graphene oxide mixed solution of diethylene glycol.
  • 专利号:   CN102897848-A
  • 发明人:   WANG Y, CHU W, YAO D, SUN Y, ZHANG H
  • 专利权人:   UNIV SOUTHEAST
  • 国际专利分类:   B82Y030/00, C01B031/04, C01G049/08
  • 专利详细信息:   CN102897848-A 30 Jan 2013 C01G-049/08 201342 Pages: 5 Chinese
  • 申请详细信息:   CN102897848-A CN10393960 17 Oct 2012
  • 优先权号:   CN10393960

▎ 摘  要

NOVELTY - A nanometer ferroferric oxide loaded graphene composite is prepared by preparing 5-15 mg/ml mixed stock solution of sodium hydroxide and diethylene glycol at 120-130 degrees C, reducing the temperature to 60-70 degrees C, preparing 0.5-3.5 mg/ml graphene oxide mixed solution of diethylene glycol, performing ultrasonic dispersion, adding ferric trichloride so that quality of the graphene is 1-4 times, stirring the mixed solution under nitrogen gas protection for 0.5 h, stirring and heating to 200-240 degrees C, heating for 0.5-2 h, and taking sodium hydroxide and diethylene glycol mixed stock solution. USE - Preparation of nanometer ferroferric oxide loaded graphene composite for magnetic separation, biomedical and electromagnetic material. ADVANTAGE - Dispersion degree is high, and coverage density and particle size are controllable. DETAILED DESCRIPTION - A nanometer ferroferric oxide loaded graphene composite is prepared by preparing 5-15 mg/ml mixed stock solution of sodium hydroxide and diethylene glycol at 120-130 degrees C, reducing the temperature to 60-70 degrees C, preparing 0.5-3.5 mg/ml graphene oxide mixed solution of diethylene glycol, performing ultrasonic dispersion, adding ferric trichloride so that quality of the graphene is 1-4 times, stirring the mixed solution under nitrogen gas protection for 0.5 h, stirring and heating to 200-240 degrees C, heating for 0.5-2 h, taking sodium hydroxide and diethylene glycol mixed stock solution, adding water, heating mixed solution, separating obtained compound, and washing with ethanol.