• 专利标题:   Composite aqueous inorganic anti-corrosive paint comprises graphene oxide, zinc powder, attapulgite AT, potassium silicate, ferric oxide red, distilled water, and sodium polyacrylate.
  • 专利号:   CN104877402-A
  • 发明人:   CHANG K, DAI W, LIU C, LIU Q, RAO Y, WANG S, ZHENG Y, KANG T, JIANG Y
  • 专利权人:   UNIV CHANGZHOU
  • 国际专利分类:   C09D001/00, C09D005/10, C09D005/24, C09D007/02
  • 专利详细信息:   CN104877402-A 02 Sep 2015 C09D-001/00 201623 Pages: 5 English
  • 申请详细信息:   CN104877402-A CN10274269 27 May 2015
  • 优先权号:   CN10274269

▎ 摘  要

NOVELTY - Composite aqueous inorganic anti-corrosive paint comprises 0.1-4 wt.% graphene oxide, 22-34 wt.% zinc powder, 1-3 wt.% attapulgite AT, 15-18 wt.% potassium silicate, 11 wt.% ferric oxide red, 30-45 wt.% distilled water, and 0.2-0.8 wt.% sodium polyacrylate. USE - Used as composite aqueous inorganic anti-corrosive paint. ADVANTAGE - The paint can greatly reduce use amount of zinc powder, increases coating conductivity and hardness, is prepared by simple process, is environmentally friendly, has good anti-corrosive property, and is applicable to all types of metal pipes and metal components. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing composite aqueous inorganic anti-corrosive paint comprising (i) mixing graphene oxide and zinc powder, stirring at 60-70 degrees C into powder, (ii) using potassium silicate, ferric oxide red, distillation water, at 35-45 degrees C, stirring, mixing to prepare base material, and (iii) mixing powder and base material and attapulgite AT, coating at 50-55 degrees C and stirring.