• 专利标题:   Graphene carbon fiber composition for fabricating high-performance carbon fiber comprises a composition for fabricating carbon fiber; and graphene powder.
  • 专利号:   US2014018480-A1, KR2014008942-A, KR1432541-B1
  • 发明人:   LEE J K, CHOI W K
  • 专利权人:   LEE J K, CHOI W K, KOREA INST SCI TECHNOLOGY
  • 国际专利分类:   C08K003/04, C08K005/20, D01D001/02, D01F001/10, D01F009/14, D01F009/22
  • 专利详细信息:   US2014018480-A1 16 Jan 2014 C08K-005/20 201408 Pages: 9 English
  • 申请详细信息:   US2014018480-A1 US939349 11 Jul 2013
  • 优先权号:   KR076759

▎ 摘  要

NOVELTY - A graphene carbon fiber composition (C1) comprises a composition for fabricating carbon fiber; and graphene powder, where the composition for fabricating carbon fiber comprises polyacrylonitrile (PAN)-based carbon fiber, pitch-based carbon fiber, and/or rayon-based carbon fiber, and the graphene powder serves as a seed of graphite to be formed during carbon fiber fabricating processes. USE - For fabricating high-performance carbon fiber (or graphite fiber). ADVANTAGE - The graphene carbon fiber composition fabricates high-performance carbon fiber with lowering a graphitization temperature. The high-performance carbon fiber indicates carbon fiber having excellent physical property i.e. tensile modulus of greater than or equal to 350 GPa. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for fabricating high-performance carbon fiber involving a mixing step to fabricate a graphene suspension by mixing a composition for fabricating carbon fiber with graphene powder to form the composition (C1), and dispersing the composition (C1) in a solvent; fiberization step to fabricate fibers by controlling a viscosity of the graphene suspension; stabilization step stabilize the fibers by heating at 200-400 degrees C under atmosphere; and heat treatment step of fabricating nano ribbon-shaped graphite by graphitizing the stabilized fibers at a temperature less than 2500 degrees C, where the graphene powder included in the composition (C1) serves as a seed of graphite to be formed during high-performance carbon fiber fabricating processes.