▎ 摘　　要

NOVELTY - Dispersion (a) formed using e.g. surface-treated graphite oxide, polyethylene oxide-polypropylene oxide-polyethylene oxide triblock copolymer and ethylene glycol, and dispersion (b) formed using e.g. ethylene glycol solution of nickel chloride are mixed, heated, cooled, centrifuged, washed, dried, obtained product and aniline are added to solution of sodium dodecylbenzenesulfonate and dispersed. Solution of ammonium persulfate and water is dripped, stirred, filtered, washed and dried, to obtain composite wave-absorbing material. USE - Preparation of nanonickel-loaded graphene composite wave-absorbing material (claimed). ADVANTAGE - The method enables rapid preparation of nanonickel-loaded graphene composite material having excellent wave absorbing performance. DETAILED DESCRIPTION - Graphite powder, potassium persulfate, phosphorus pentoxide and concentrated sulfuric acid in a molar ratio of 1-3:1-2:1-2:5-10 are mixed, pH is adjusted to 1.5, then stirred at 60 degrees C for 1-2 hours, heated at 80 degrees C for 2-4 hours at a rate of 5 degrees C/minute, stirred at 87 degrees C for 1-2 hours at a rate of 2 degrees C/minute, diluted using distilled water, pH is adjusted to 3.6, leave still for 36 hours, filtered and solid is dried at room temperature. Concentrated nitric acid is added, stirred for 45-60 minutes, pH is adjusted to 2-4, potassium permanganate is added at -8 degrees C, stirred for 30 minutes, cooled to -12 degrees C, potassium permanganate is further added, stirred for 30 minutes, cooled to -15 degrees C, potassium permanganate is added and stirred for 20 minutes. Mixture is heated at 40 degrees C for 3 hours in an incubator, distilled water is added, reacted at 40 degrees C for 2.5 hours, distilled water and hydrogen peroxide in a ratio of 4-20:1 are added, mixed for 10-60 minutes, centrifuged for 10 minutes at a rate of 9500 rpm, washed using hydrochloric acid solution, where the volume of hydrochloric acid solution after centrifugation is 10-50 times the volume of the product, and dialyzed for 7-8 days, to obtain graphite oxide. Graphite oxide is purified using 1.72 g/ml concentrated sulfuric acid and hydrogen peroxide in a mass ratio of 1-2:2-5. Purified graphite oxide is dissolved in dimethyl sulfoxide, then N- hydroxysuccinimide and surfactant are added, stirred at 35 degrees C for 2 hours, filtered, washed and dried, to obtain surface-treated graphite oxide. 1-2 g Surface-treated graphite oxide is freeze-dried at -10 degrees C to -30 degrees C, 1-10 g polyethylene oxide-polypropylene oxide-polyethylene oxide triblock copolymer and 1 g polymethylmethacrylate-polyacrylamide are added, mixed, mixture is dispersed in 500 ml ethylene glycol, and irradiated with ultraviolet radiation for 36 hours, to obtain uniform dispersion (a). 20-40 Ml ethylene glycol solution of nickel chloride with concentration of 0.1 mol/ml, 6-25 g polyvinylpyrrolidone and 10-50 g ammonium acetate are dissolved in 500-1000 ml ethylene glycol, to obtain dispersion (b). Dispersion (a) and dispersion (b) are mixed, and pH is adjusted to 9-11 using ammonia. 100 ml Obtained solution is added into reactor, then sealed and heated at 130 degrees C for 2 hours at a rate of 2-4 degrees C/minute, further heated at 150 degrees C for 4 hours at a rate of 3-6 degrees C/minute, heated at 200 degrees C for 3 hours, cooled to 180 degrees C at a rate of 5-7 degrees C/minute, heated at 200 degrees C for 7 hours at a rate of 3-6 degrees C/minute, cooled to room temperature at a rate of 3-6 degrees C/minute, centrifuged for 10 minutes at a rate of 8000-10000 rpm, washed 3 times using ethanol and deionized water, and vacuum-dried at 50-70 degrees C for 24 hours, to obtain dried product (A). 5 g Product (A) and 5-10 g aniline monomer are added to a solution of sodium dodecylbenzenesulfonate and ultrasonically dispersed for 65 minutes, to obtain product (B). Solution of 3 g ammonium persulfate dissolved in 80-120 ml distilled water is dripped into product (B), stirred for 15 hours, filtered, washed using distilled water and ethanol, and vacuum-dried at 50-70 degrees C for 24-36 hours, to obtain nanonickel-loaded graphene composite wave-absorbing material. The ratio of dried substance and concentrated nitric acid is 1-4:50-100. The mass ratio of dried substance and total amount of potassium permanganate is 1-2:10-15. The mass ratio of product (A) and sodium dodecylbenzenesulfonate is 1-1.5:8-15. An INDEPENDENT CLAIM is included for nanonickel-loaded graphene composite wave-absorbing material, which is a layered composite material comprising nickel nanoparticles having particle size of 20-100 nm, grown on a graphene sheet layer, and polyaniline coated on the surface of the graphene sheet loaded with the nickel nanoparticles.