• 专利标题:   Composite material curing agent useful for sulfoaluminate cement, comprises sulfur aluminate cement, graphene oxide, polycarboxylic acid high-efficiency water reducing agent, and curing agent provided with pore canal for ion diffusion.
  • 专利号:   CN113149575-A
  • 发明人:   WANG Z, YANG F, ZHOU X
  • 专利权人:   UNIV SOUTHEAST
  • 国际专利分类:   C04B028/06
  • 专利详细信息:   CN113149575-A 23 Jul 2021 C04B-028/06 202165 Pages: 11 Chinese
  • 申请详细信息:   CN113149575-A CN10409742 15 Apr 2021
  • 优先权号:   CN10409742

▎ 摘  要

NOVELTY - Composite material curing agent comprises 90-100 pts. wt. sulfoaluminate cement , 0.01-0.1 pts. graphene oxide , 0.8-1.2 pts. polycarboxylic acid high-efficiency water reducing agent, where the curing agent is provided with a pore canal for ion diffusion and promoting hydration of sulfoaluminate cement. The graphene oxide is nano-sized particles prepared by the Hummer freeze-drying method. USE - The composite material curing agent is useful for sulfoaluminate cement. ADVANTAGE - The curing agent has higher adsorption/curing capacity, better adsorption/curing effect, low cost, simple operation, short flow, no secondary pollution, and promotes hydration of wet surface air cooler. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing the composite material curing agent.