• 专利标题:   Preparation of composite material involves dispersing mono-layered graphene oxide in solvent, adding ultra-high molecular weight polyethylene, stirring, drying, pre-pressing, cooling, and irradiating with electronic beam.
  • 专利号:   CN104327357-A
  • 发明人:   CHEN G, HUANG G, NI Z, ZHAO Z, PANG W
  • 专利权人:   UNIV JIANGNAN
  • 国际专利分类:   B29C035/02, C08J003/28, C08K003/04, C08K009/00, C08L023/06
  • 专利详细信息:   CN104327357-A 04 Feb 2015 C08L-023/06 201531 Pages: 6 Chinese
  • 申请详细信息:   CN104327357-A CN10622515 08 Nov 2014
  • 优先权号:   CN10622515

▎ 摘  要

NOVELTY - Preparation of composite material involves dispersing 0.1-5 pts. wt. mono-layered graphene oxide in 500 pts. wt. solvent, ultrasonically processing, adding 95-99.9 pts. wt. ultra-high molecular weight polyethylene, stirring, drying resultant product, milling, pre-pressing in a flat vulcanizing machine at 4-9 MPa for 10-30 minutes, heat-preserving at 180-250 degrees C for 1.5-3 hours, processing in a lower die at 8-20 MPa, cooling to room temperature, and irradiating with electronic beam or radioactive source of cobalt at exposure dose of 50-150 kGy for 5-9 days. USE - Preparation of composite material (claimed). ADVANTAGE - The method enables preparation of composite material having excellent mechanical property, hardness, tensile strength, frictional resistance and wear resistance. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for composite material.