• 专利标题:   Amphiphobic type high weather resistance aqueous finishing coat comprises resin, graphene, lotus leaf element, auxiliary agent, pigment and filler, solvent, water-dispersible polyisocyanate and propylene glycol diacetate.
  • 专利号:   CN107163739-A
  • 发明人:   XIE Y, ZHANG X
  • 专利权人:   ZHANGZHOU XINZHANWANG CHEM CO LTD
  • 国际专利分类:   C09D133/00, C09D005/02, C09D005/16, C09D007/12
  • 专利详细信息:   CN107163739-A 15 Sep 2017 C09D-133/00 201778 Pages: 5 Chinese
  • 申请详细信息:   CN107163739-A CN10557306 10 Jul 2017
  • 优先权号:   CN10557306

▎ 摘  要

NOVELTY - Amphiphobic type high weather resistance aqueous finishing coat comprises component A and component B, where the component A includes 35-45 wt.% resin, 5-8 wt.% graphene, 3-5 wt.% lotus leaf element, 3-5 wt.% auxiliary agent, 15-20 wt.% pigment and filler and 27-30 wt.% solvent, the component B includes 60-70 wt.% water-dispersible polyisocyanate and 30-40 wt.% propylene glycol diacetate. USE - Used as amphiphobic type high weather resistance aqueous finishing coat. ADVANTAGE - The finishing coat: has good wear resistance, impact resistance and weather resistance; use in material e.g. car surface has good protection effect so as to prolong its service life. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for use method of amphiphobic type high weather resistance aqueous finishing coat, comprising mixing resin, graphene, lotus leaf pigment, auxiliary agent, pigment and filler uniformly, adding solvent under the condition of stirring, immediately stirring at 1000 revolutions/minute for dispersing for 30 minutes, grinding till fineness of not greater than 15 mu m to obtain component A, mixing water-dispersible polyisocyanate and propylene glycol diacetate to obtain as component B, at the construction site, mixing the component A and component B according to 3:1 weight ratio, spraying directly, baking at 70 degrees C for 40-50 minutes, and coating as film to thickness of 35-45 mu m.