• 专利标题:   Preparing aqueous polyurethane coating having weathered and sand abrasion resistance useful for wind turbine blades, comprises e.g. adding molybdenum disulfide as polyphenol-modified two-dimensional nanosheets to aqueous polyurethane coating emulsion, and stirring.
  • 专利号:   CN115785782-A
  • 发明人:   LIU J, ZHOU P, ZHANG X
  • 专利权人:   UNIV SICHUAN
  • 国际专利分类:   C09D175/04, C09D007/62, C09D007/63, C09D007/65
  • 专利详细信息:   CN115785782-A 14 Mar 2023 C09D-175/04 202326 Chinese
  • 申请详细信息:   CN115785782-A CN11551201 05 Dec 2022
  • 优先权号:   CN11551201

▎ 摘  要

NOVELTY - Preparing aqueous polyurethane coating having weathered and sand abrasion resistance, comprises preparing aqueous polyurethane coating emulsion, adding 1-40 pts. wt. polyphenol-modified two-dimensional nanosheets to 100 pts. wt. aqueous polyurethane coating emulsion, and stirring until completely dispersed to obtain final product in which polyphenol-modified two-dimensional nanosheet is two-dimensional nanosheet material whose surface is modified with many phenolic hydroxy groups, and the phenolic hydroxy group is connected to the two-dimensional nanosheet by reversible non-covalent π-π conjugated bond. USE - The aqueous polyurethane coating is useful for wind turbine blades (claimed). ADVANTAGE - The aqueous polyurethane coating has low production costs, mild preparation conditions, simple processing steps, and excellent wear resistance.