▎ 摘　　要

NOVELTY - Concentrated graphene polymer comprises graphene nanoflake core, double soluble surfactant, and nonionic surface active gel. USE - The Concentrated graphene polymer is useful for oil and gas exploitation, and geothermal development, conduction, energy saving, infiltration, anti-corrosion fields. DETAILED DESCRIPTION - INDEPENDENT CLAIMS are also included for: (1) preparing concentrated graphene polymer comprising (i) providing double-soluble surfactant, nonionic surfactant, and ethanol or propanol volatile environmentally-friendly dispersing agent having volume greater than 1 times and boiling point lower than 100 degrees C, mixing, uniformly stirring mixture to obtain graphene dispersion, (ii) placing graphene dispersion in pressure-resistant and temperature-resistant non-metallic closed container, performing microwave heating at 90-100 degrees C until the volatile dispersant is completely evaporated and vaporized and other surfactants around the graphene concentrated film forms highly dispersed graphene film foam, and (iii) stirring or ultrasonically vibrating during highly-dispersed graphene film-forming foam formed in the pressure-resistant and temperature-resistant non-metallic container releases gas to normal pressure, cooling to normal temperature, and condensing into concentrated graphene polymer; and (2) graphene polyadipide nano-foam/graphene poly-gel hot water or steam/graphene poly-adhesive nano-emulsion/graphene poly-adhesive nano acid/graphene poly-colloid nano-alkali/graphene poly-adhesive nano paint/graphene poly-adhesive nano-cement slurry/graphene poly-adhesive nano-resin pulp, the graphene polyadipide nano-foam is graphene thick polycondensate prepared by diluting with water and introducing an inert gas, the graphene polyglycol hot water or steam is prepared by heating and diluting concentrated graphene polymer with water, the graphene polymer nanoemulsion is prepared by diluting the concentrated graphene polymer with an emulsion, the graphene polyadipizing nano acid solution is prepared by diluting concentrated graphene polymer with an organic acid solution or an inorganic acid solution, the graphene polycolloid nano alkali is prepared by diluting concentrated graphene polymer with alkali solution, the graphene polyadhesive nano-paste is prepared by diluting concentrated graphene polymer with a paint, the graphene polycolloid nanoporous cement slurry is prepared by diluting concentrated graphene polymer with a slurry, graphene polyadipide nanoresin is prepared by diluting concentrated graphene polymer with resin.