▎ 摘　　要

NOVELTY - Cast iron nickel molybdenum aluminum-silicon-iron alloy supported nano-composite is composed of 2-3 pts. wt. nano-alumina, 1-2 pts. wt. fluorine, 2-3 pts. wt. nickel powder, 1-2 pts. wt. aluminum powder, 1-2 pts. wt. molybdenum powder, 0.2-0.4 pts. wt. graphene oxide, 1-2 pts. wt. silicon dioxide, 3-5 pts. wt. expanded graphite powder, 1-2 pts. wt. monazite powder whose silicon content is 45%, 4-5 pts. wt. ferrosilicon powder, 0.3-0.4 pts. wt. magnesium aluminum silicate, 20-25 pts. wt. 5-10% ethanol solution and 0.4-0.5 pts. wt. auxiliary agent. USE - Cast iron nickel molybdenum aluminum-silicon-iron alloy supported nano-composite used in ball milling. ADVANTAGE - Modifier promotes the graphitization process, thus reducing the production cost. DETAILED DESCRIPTION - Cast iron nickel molybdenum aluminum-silicon-iron alloy supported nano-composite is composed of 2-3 pts. wt. nano-alumina, 1-2 pts. wt. fluorine, 2-3 pts. wt. nickel powder, 1-2 pts. wt. aluminum powder, 1-2 pts. wt. molybdenum powder, 0.2-0.4 pts. wt. graphene oxide, 1-2 pts. wt. silicon dioxide, 3-5 pts. wt. expanded graphite powder, 1-2 pts. wt. monazite powder whose silicon content is 45%, 4-5 pts. wt. ferrosilicon powder, 0.3-0.4 pts. wt. magnesium aluminum silicate, 20-25 pts. wt. 5-10% ethanol solution and 0.4-0.5 pts. wt. auxiliary agent. Auxiliary agent is composed of 2-3 pts. wt. potassium feldspar, 1-3 pts. wt. lithium slag. 2-3 pts. wt. yttrium rare earth nucleating agent, 0.5-0.8 pts. wt. boron phosphate, 2-3 pts. wt. carbon fiber, 1-2 pts. wt. sodium lignosulfonate, 2-3 pts. wt. organic bentonite, 15-20 pts. wt. water. Preparation involves mixing sodium lignin sulfonate and organic bentonite for 40-50 minutes, milling potassium feldspar and lithium slag, passing through 80-120 mesh sieve, grinding in activation liquid for 1-2 hours and adding the remaining ingredients into the activated slurry.