• 专利标题:   Lithium-air cell catalyst comprises perovskite lanthanum strontium cobalt oxide particles with graphene composite, where lanthanum strontium cobalt oxide particles have lanthanum strontium cobalt oxide nanoparticles.
  • 专利号:   CN104538647-A, CN104538647-B
  • 发明人:   WANG Q, WANG Z, DING C
  • 专利权人:   HEFEI GUOXUAN HIGH TECH POWER SOURCE CO
  • 国际专利分类:   B01J023/83, H01M004/90
  • 专利详细信息:   CN104538647-A 22 Apr 2015 H01M-004/90 201548 Pages: 8 Chinese
  • 申请详细信息:   CN104538647-A CN10001263 04 Jan 2015
  • 优先权号:   CN10001263

▎ 摘  要

NOVELTY - The lithium-air cell catalyst comprises perovskite lanthanum strontium cobalt oxide (LSCO) particles with a graphene composite, where the lanthanum strontium cobalt oxide particles have lanthanum strontium cobalt oxide nanoparticles with a diameter of 15-30 nm. The nanoparticles are adsorbed on surface of graphene. USE - Lithium-air cell catalyst. ADVANTAGE - The lithium-air cell catalyst ensures good catalytic performance, very high capacitance, and cane be manufactured in a simple, cost-effective and environment-friendly manner. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for a method for preparing lithium-air cell catalyst, which involves: (A) dispersing 40 mg graphite oxide in 40 ml deionized water with stirring for 1 hour to obtain a homogeneous graphene oxide solution; (B) dissolving lanthanum compound, strontium compound and a cobalt compound in deionized water uniformly to prepare an aqueous solution; (C) adding the formed aqueous solution in the obtained homogeneous graphene oxide solution with stirring to obtain a solution in a reaction vessel; (D) heating the formed solution at 140-200 degrees C for 5-20 hours to obtain a precipitate; (E) filtering and washing the formed precipitate with deionized water; (F) drying the washed precipitate; (G) adding hydrazine hydrate to perform hydrothermal reaction at 100-150 degrees C for 1-5 hours; (H) cooling the mixture at room temperature to give another precipitate; (I) washing the formed precipitate repeatedly with deionized water and ethanol; and (J) drying at 400-700 degrees C under inert atmosphere for 2-20 hours to get the finished product.