▎ 摘　　要

NOVELTY - Production of micro/mesoporous conductive polymer involves adding an aqueous suspension of a graphene oxide with a concentration of 1-10 g/L to a hydrazine in a ratio of 1:1-10:1, vigorously stirring at room temperature for 60 seconds, maintaining the temperature at 40-80° C for 15 minutes-2 hours, filtering the obtained gelling product and drying to a humidity level of 200-400%, and annealing the gelling product at 150-900° C for 10-1440 minutes under an atmosphere of hydrogen at an absolute pressure of 100 Pa-1 MPa. USE - Production of micro/mesoporous conductive polymer. ADVANTAGE - The method provides conductive polymer having spatial structure of graphene and high active surface.