• 专利标题:   Graphene-doped manganese oxide carbon cloth-based flexible composite electrode preparation involves adding graphene to aqueous solution of dispersant graphene water dispersant, and ultrasonically dispersing to obtain mixed solution.
  • 专利号:   CN111627728-A
  • 发明人:   YE Z, WU K, LI D, PENG X
  • 专利权人:   UNIV NANCHANG HANGKONG
  • 国际专利分类:   C25D005/06, C25D005/54, C25D009/04, H01G011/28, H01G011/46, H01G011/86
  • 专利详细信息:   CN111627728-A 04 Sep 2020 H01G-011/86 202080 Pages: 11 Chinese
  • 申请详细信息:   CN111627728-A CN10695929 20 Jul 2020
  • 优先权号:   CN10695929

▎ 摘  要

NOVELTY - Graphene-doped manganese oxide carbon cloth-based flexible composite electrode preparation involves adding 0.1~5.0 mg mL1 graphene to aqueous solution of 0.02-1.0 mg mL1 dispersant graphene water dispersant (TNRDIS), and ultrasonically dispersing for 40-80 minutes to obtain a mixed solution of graphene water dispersion and 0.1~0.5 molL1 manganese sulfate solution as a brush plating solution. USE - Method for preparing the graphene-doped manganese oxide carbon cloth-based flexible composite electrode for folding equipment, wearable sensors, aerospace and other fields. ADVANTAGE - The method prepares the graphene-doped manganese oxide carbon cloth-based flexible composite electrode in a simple, cost-effective and eco-friendly manner with high preparation efficiency, high bonding strength with matrix, excellent mechanical properties, high energy density, low internal resistance and high specific capacitance.