• 专利标题:   Preparing environmental catalytic material involves impregnating textile fiber with saturated dispersion of graphene oxide, drying, washing, and then placing in a reducing atmosphere.
  • 专利号:   CN106076426-A
  • 发明人:   LIU B, ZHOU D, ZHU Z
  • 专利权人:   UNIV DONGHUA
  • 国际专利分类:   B01J031/26, B01J035/10, C02F001/30, C02F001/72
  • 专利详细信息:   CN106076426-A 09 Nov 2016 B01J-031/26 201702 Pages: 7 Chinese
  • 申请详细信息:   CN106076426-A CN10395282 06 Jun 2016
  • 优先权号:   CN10395282

▎ 摘  要

NOVELTY - Preparing environmental catalytic material involves impregnating a textile fiber with a saturated dispersion of graphene oxide, drying, washing, and then placing in a reducing atmosphere, which is added with bismuth(III) nitrate and the nitric acid solution to obtain the textile fiber/graphene, where the ratio of bismuth(III) nitrate and the nitric acid is 1:1. The obtained product is added with sodium hydroxide, sodium bromide and and potassium iodide, followed by hydrothermal reaction at 120-180 degrees C for 3-8 hours, cooled, washed and dried. USE - Method for preparing environmental catalytic material (claimed). ADVANTAGE - The method enables to prepare environmental catalytic material in simple manner, that has better environmental purification effect and is suitable for industrial production. DETAILED DESCRIPTION - Preparing environmental catalytic material involves impregnating a textile fiber with a saturated dispersion of graphene oxide, drying, washing, and then placing in a reducing atmosphere, which is added with bismuth(III) nitrate and the nitric acid solution to obtain the textile fiber/graphene, where the ratio of bismuth(III) nitrate and the nitric acid is 1:1. The obtained product is added with sodium hydroxide, sodium bromide and and potassium iodide, followed by hydrothermal reaction at 120-180 degrees C for 3-8 hours, cooled, washed and dried to obtain textile fiber/graphene/ bismutoxidbromid/bismuth oxyiodide composite based environment catalytic material.