• 专利标题:   Microcrystalline jade decorating material based on graphene includes stone tail mineral, silicon dioxide, graphite, silicon carbide crystal whisker, feldspar, soda feldspar, calcium carbonate, zinc oxide and inorganic pigment.
  • 专利号:   CN107572826-A, CN107572826-B
  • 发明人:   HUANG Y, HUANG Z
  • 专利权人:   GUANGXI XUTENG IND GROUP CO LTD
  • 国际专利分类:   C03B011/00, C03B032/02, C03C010/00, C03C006/02
  • 专利详细信息:   CN107572826-A 12 Jan 2018 C03C-010/00 201809 Pages: 11 Chinese
  • 申请详细信息:   CN107572826-A CN11047315 31 Oct 2017
  • 优先权号:   CN11047315

▎ 摘  要

NOVELTY - Microcrystalline jade decorating material based on graphene includes 20-70 pts. wt. stone tail mineral, 20-75 pts. wt. silicon dioxide, 1-15 pts. wt. graphite, 1-5 pts. wt. silicon carbide crystal whisker, 1-10 pts. wt. feldspar, 1-10 pts. wt. soda feldspar, 0-20 pts. wt. aluminum oxide or aluminum hydroxide, 1-15 pts. wt. high-temperature cosolvent, 10-40 pts. wt. calcium carbonate, 0-5 pts. wt. zinc oxide, 0-10 pts. wt. zirconium oxide, 1-8 pts. wt. yttrium oxide, 0-5 pts. wt. diantimony trioxide, 0.05-5 pts. wt. adhesive agent, 0.05-5 pts. wt. stabilizer, and 0-5 pts. wt. inorganic pigment. USE - Microcrystalline jade decorating material based on graphene. ADVANTAGE - The material has transparent or semitransparent jade structure. DETAILED DESCRIPTION - Microcrystalline jade decorating material based on graphene comprises 20-70 pts. wt. stone tail mineral, 20-75 pts. wt. silicon dioxide, 1-15 pts. wt. graphite, 1-5 pts. wt. silicon carbide crystal whisker, 1-10 pts. wt. feldspar, 1-10 pts. wt. soda feldspar, 0-20 pts. wt. aluminum oxide or aluminum hydroxide, 1-15 pts. wt. high-temperature cosolvent, 10-40 pts. wt. calcium carbonate, 0-5 pts. wt. zinc oxide, 0-10 pts. wt. zirconium oxide, 0-5 pts. wt. barium carbonate, 1-5 pts. wt. boron oxide, 1-10 pts. wt. sodium carbonate, 1-8 pts. wt. titanium dioxide, 1-8 pts. wt. yttrium oxide, 0-5 pts. wt. diantimony trioxide, 0.05-5 pts. wt. adhesive agent, 0.05-5 pts. wt. stabilizer, and 0-5 pts. wt. inorganic pigment. An INDEPENDENT CLAIM is included for preparation of microcrystalline jade decorating material based on graphene comprising weighing raw materials, mixing, crushing, ball milling for 3-15 hours, sieving, putting into storehouse, and homogenizing to obtain mixed material; melting mixed material for 4.0 hours at 1460-1560 degrees C, keeping temperature for 1-3 hours, homogenizing at 1350-1500 degrees C, clarifying solution, and obtaining high temperature melt; calendering or steel molding to form blank; putting blank into crystallization annealing kiln furnace, annealing at 800-900 degrees C for 2-8 hours, 700-800 degrees C for 2-6 hours, 600 degrees C for 2-6 hours, and cooling naturally to obtain crude product; and grinding, polishing, cutting and forming.