• 专利标题:   Graphene microsphere, prepared by dissolving the expanded graphite in deionized water, adding surfactant, ultrasonically stirring, adding into titanium source solution. ultrasonically stirring, adding ammonia water, and stirring.
  • 专利号:   CN111252755-A
  • 发明人:   CHEN L
  • 专利权人:   YUYAO JINGPENG PHOTOVOLTAIC POWER GENERATION CO LTD
  • 国际专利分类:   C01B032/19, H01M004/62
  • 专利详细信息:   CN111252755-A 09 Jun 2020 C01B-032/19 202052 Pages: 6 Chinese
  • 申请详细信息:   CN111252755-A CN11450390 30 Nov 2018
  • 优先权号:   CN11450390

▎ 摘  要

NOVELTY - Graphene microsphere, is claimed. The preparation of graphene microsphere comprises (i) adding graphite into a mixed solution consisting of concentrated sulfuric acid and potassium permanganate, and ultrasonically stirring at 20-60 degrees C for 0.5-5 hours, washing the resulting product, filtering and drying, in a muffle furnace, treating in a nitrogen atmosphere at 600-1200 degrees C for 0.1-6 hours to obtain expanded graphite products; (ii) dissolving the expanded graphite in deionized water, adding 0.1-5 wt.% surfactant, ultrasonically stirring, gradually adding into titanium source solution; ultrasonically stirring for 0.5-4 hours, adding ammonia water, ultrasonically stirring, spray-drying the resulting mixture solution, placing the resulting product in a muffle furnace protected by a special atmosphere, treating, washing the resulting product with dilute acid or alkali and deionized aqueous solution for many times, vacuum drying in a vacuum drying oven. USE - Used as graphene microsphere. DETAILED DESCRIPTION - Graphene microsphere, is claimed. The preparation of graphene comprises (i) adding graphite into a mixed solution consisting of concentrated sulfuric acid and potassium permanganate, and ultrasonically stirring at 20-60 degrees C for 0.5-5 hours, washing the resulting product, filtering and drying, in a muffle furnace, treating in a nitrogen atmosphere at 600-1200 degrees C for 0.1-6 hours to obtain expanded graphite products; (ii) dissolving the expanded graphite in deionized water, adding 0.1-5 wt.% surfactant, ultrasonically stirring for 0.1-2 hours, gradually adding into titanium source solution, where the mass ratio of the titanium source to the expanded graphite precursor is 0.1-20:1; ultrasonically stirring for 0.5-4 hours, adding ammonia water, where the molar ratio of the ammonia water to the titanium source is 1-10:1, ultrasonically stirring for 0.5-4 hours, spray-drying the resulting mixture solution, placing the resulting product in a muffle furnace protected by a special atmosphere, treating at 600-1200 degrees C for 0.1-6 hours, washing the resulting product with dilute acid or alkali and deionized aqueous solution for many times, vacuum drying in a vacuum drying oven for 0.5-8 hours.