• 专利标题:   Composite phase change nanofiber material is polyethylene glycol, supporting material is polyvinylpyrrolidone, and heat conducting material is graphene oxide.
  • 专利号:   CN108754661-A
  • 发明人:   ZHANG H, JI R, XIA Y, WEI S, HUANG C, LI Z, MO X, SUN L, XU F
  • 专利权人:   UNIV GUILIN ELECTRONIC TECHNOLOGY
  • 国际专利分类:   D01F006/56, D01F001/10, D01D005/00, C09K005/02
  • 专利详细信息:   CN108754661-A 06 Nov 2018 D01F-006/56 201903 Pages: 6 Chinese
  • 申请详细信息:   CN108754661-A CN10772149 13 Jul 2018
  • 优先权号:   CN10772149

▎ 摘  要

NOVELTY - Composite phase change nanofiber material is polyethylene glycol, supporting material is polyvinylpyrrolidone, and heat conducting material is graphene oxide. USE - Composite phase change nanofiber material. ADVANTAGE - The composite phase change nanofiber material has simple proces, easy to adjust process parameter, improved thermal conductivity, and effectively prevents leakage during solid-liquid phase transition. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for a method for preparing a composite phase change nanofiber material, which involves: (A) preparing graphene oxide by Hummers method, dissolving graphene oxide in N,N-dimethylformamide, and performing ultrasonic reaction so that it is completely dissolve to obtain a solution; (B) preparing an electrospinning solution by adding polyvinylpyrrolidone and polyethylene glycol in the solution, and stirring it under certain conditions so that it is completely dissolved; and (C) carrying out high-voltage electrospinning by electrospinning the mixed solution at room temperature, and placing composite phase-change nanofiber material in an oven to completely volatilize N,N-dimethylformamide to obtain final product.