▎ 摘　　要

NOVELTY - Preparing graphene modified antistatic fabric, comprises adding three-dimensional structure graphene powder into the N,N-dimethylformamide solvent, and uniformly dispersing under the action of ultrasound for 3-5 hours, adding triethylamine and silane coupling agent and stirring, transferring to the reaction kettle, passing nitrogen to discharge the residual air in the reaction kettle, carrying out the heating reaction, and collecting the functionalized modified three-dimensional structure graphene powder by centrifugation, dissolving secondary distilled aniline in an aqueous sulfuric acid solution, stirring at room temperature, continuously adding the functionalized modified three-dimensional structure graphene powder and stirring, dropping ammonium persulfate, refrigerating and placing, and filtering precipitate and washing, and drying in a vacuum drying box to obtain a functionalized modified three-dimensional structure graphene powder doped with polyaniline, USE - The method is useful for preparing graphene modified antistatic fabric. ADVANTAGE - The method enables to prepare graphene modified antistatic surface fabric that has high specific surface area, high conductivity and low cost, silane functionalized modified to realize good hydrophobic and mechanical property, polyaniline has excellent conductivity, and micro-characteristics, thus greatly improves the anti-static ability of the whole, fibrosis, to obtain the graphene modified antistatic fabric, the manufacturing cost is lower, it has strong adaptability, and can realize the preparation of the fabric by multiple mixed weaving or interweaving method.