▎ 摘　　要

NOVELTY - Method for preparing graphene conductive material involves: (a) adding graphene oxide into deionized water, adding phosphoric acid, uniformly stirring, adding lithium hydroxide, stirring and mixing for 30-40 minutes, introducing nitrogen, orderly adding ferrous sulfate and glucose, uniformly stirring, sending into reaction kettle, reacting for 10-12 hours at 200-240degrees Celsius, discharging, washing precipitate with absolute ethanol for 2-3 times, and drying for 10-12 hours at 50-55degrees Celsius to obtain modified graphene; (b) mixing modified graphene with dispersant, ultrasonically dispersing, adding metal salt solution, and ultrasonically dispersing; and (c) placing metal base film in solution, reacting for 3-4 hours at 85-95degrees Celsius by using hydrothermal method, and drying at 70-80degrees Celsius. USE - Preparation method of graphene conductive material used in application field of lithium battery, printed circuit and electronic component i.e. capacitor, energy, metal anti-corrosion and biosensor, and preparing nano-composite material with high performance. ADVANTAGE - The method provides graphene conductive material with good conductivity and mechanical property.