• 专利标题:   Graphene modified polyvinylchloride material comprises polyvinyl chloride, lightweight calcium carbonate, stabilizer, ACR-201, ACR-901, titanium dioxide, paraffin, polyethylene wax, brightener and graphene.
  • 专利号:   CN105131450-A
  • 发明人:   CHEN W, HU K, ZHOU M
  • 专利权人:   NINGBO HUAAN BUILDING MATERIAL SMELTER
  • 国际专利分类:   C08K013/02, C08K003/04, C08K003/22, C08K003/26, C08L023/06, C08L027/00, C08L033/04, C08L091/06
  • 专利详细信息:   CN105131450-A 09 Dec 2015 C08L-027/00 201607 Pages: 6 English
  • 申请详细信息:   CN105131450-A CN10515684 21 Aug 2015
  • 优先权号:   CN10515684

▎ 摘  要

NOVELTY - Graphene modified polyvinylchloride material comprises 100 pts. wt. polyvinyl chloride, 10-15 pts. wt. lightweight calcium carbonate, 3.5-4 pts. wt. stabilizer, 5-7 pts. wt. ACR-201, 1-3 pts. wt. ACR-901, 3-4 pts. wt. titanium dioxide, 0.1-0.3 pts. wt. paraffin, 0.4-0.7 pts. wt. polyethylene wax, 0.01-0.014 pts. wt. brightener and 1.5-4 pts. wt. graphene. USE - Used as graphene modified polyvinylchloride material. ADVANTAGE - The material has good mechanical properties. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing graphene modified polyvinylchloride material comprising (i) mixing all raw materials in a mixer at 100-150 degrees C, again mixing at 35-50 degrees C; (ii) carrying out extrusion of mixed material into a extruder under pressure 15-25MPa, and water-cooling; and (iii) carrying out traction using traction machine and cutting.