▎ 摘　　要

NOVELTY - Fiber concrete comprises 505 pts. wt. cement, 70 pts. wt. water, 1000 pts. wt. gravel, 770 pts. wt. aggregate, 70 pts. wt. fly ash, 78 pts. wt. rice hull ash, 118 pts. wt. silicon ash, 15 pts. wt. water reducing agent, 10 pts. wt. activator, 1.7 pts. wt. cellulose fiber, 43 pts. wt. hydroxy-modified carbon nano tube dispersing liquid, 45 pts. wt. graphene oxide dispersion, and 2.7 pts. wt. antifoaming agent. USE - Used as fiber concrete. ADVANTAGE - The fiber concrete has C180 strength grade level, ultra-high-strength and has high-performance; ensures synergetic work performance between the section steel and concrete, making defect bonding performance of the structural steel and concrete is bad, and ensures mechanical performance. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing fiber concrete comprising (i) adding 10 pts. wt. activator and 2.7 pts. wt. efoaming agent into 25% water of total water, marked as I aqueous solution, then adding 15 pts. wt. water reducing agent, 43 pts. wt. hydroxy modified carbon nanotube dispersion liquid and 45 pts. wt. dispersion of graphene oxide into the 50% aqueous solution, marked as II aqueous solution; (ii) adding 770 pts. wt. in a mass ratio of 8:2 configuration of river sand and quartz sand, 1000 pts. wt. gravel and 1.7 pts. wt. cellulose fibers, adding to the mixer, uniformly stirring for 2-3 minutes; (iii) adding 505 pts. wt. cement, 70 pts. wt. fly ash, 78 pts. wt. rice husk ash, 118 pts. wt. silica fume, then taking step (i) of prepared in aqueous solution I, adding to the mixer, and stir for 2-3 minutes; (iv) then adding aqueous solution II in step (i) into the mixer, uniformly stirring for 3-4 minutes; and (v) observing the fluidity of the mixture, and continue to joining the remaining 25% of the total amount of water, stirring for 3-5 minutes, discharging, obtaining concrete mix, forming, and conserving.