NOVELTY - Organosilicone modified epoxy resin anticorrosive paint comprises coating component and curing component at a mass ratio of 80-90:10-20, where the coating component comprises organosilicone modified epoxy resin, pigment filler, solvent A, and auxiliary agent at a mass ratio of 42-48:10-20:20-40:10-20. The preparation of organosilicone modified epoxy resin comprises taking butyl acetate and acetone as solvent B, taking stannous octoate as catalyst, adding 50-80 pts. wt. epoxy resin E-06, 60-100 pts. wt. Wd-40 silane coupling agent, 70-100 pts. wt. solvent B, and 0.5-1 pts. wt. catalyst into the reactor, heating and reacting to 140-160 degrees C for 1-2 hours. The pigment filler comprises iron oxide red and graphene. The solvent A comprises dimethylbenzene and ethyl acetate. The curing component is low molecular weight polyamide resin. USE - Used as organosilicone modified epoxy resin anticorrosive paint.