• 专利标题:   Preparation of sandwich structure nitrogen-doped zinc oxide coated nitrogen-doped graphene composite material used as photocatalytic material, involves mixing graphene oxide dispersion with aniline, adding ammonium persulfate aqueous solution, stirring to obtain mixed solution, and calcining.
  • 专利号:   CN113559913-A
  • 发明人:   LI Y, NING X, ZENG B
  • 专利权人:   UNIV HUNAN ARTS SCI
  • 国际专利分类:   B01J027/24, C02F001/30, C02F101/34, C02F101/38
  • 专利详细信息:   CN113559913-A 29 Oct 2021 B01J-027/24 202225 Chinese
  • 申请详细信息:   CN113559913-A CN10968162 23 Aug 2021
  • 优先权号:   CN10968162

▎ 摘  要

NOVELTY - Preparation of sandwich structure nitrogen-doped zinc oxide coated nitrogen-doped graphene composite material, involves (1) mixing the graphene oxide dispersion with aniline, then adding a small amount of ammonium persulfate aqueous solution, stirring, and then continuing to add zinc acetate dihydrate aqueous solution under stirring conditions to obtain a mixed solution, (2) subjecting the mixed solution to a hydrothermal reaction to obtain an intermediate product, and (3) after filtering and drying the intermediate product, calcining under the protection of nitrogen to obtain the final product. USE - Preparation of sandwich structure nitrogen-doped zinc oxide coated nitrogen-doped graphene composite material used as photocatalytic material (all claimed). ADVANTAGE - The preparation is simple and economical, provides composite material with visible light response ability, abundant active reaction points, and excellent photogenerated electron transmission property and catalytic activity.