▎ 摘　　要

NOVELTY - Modified graphene aqueous anti-corrosion coating comprises 55-65 pts. wt. aqueous epoxy resin, 4-8 pts. wt. octadecyl amine and silane co-modified graphene oxide, 2-4 pts. wt. silane- modified zinc-copper-iron hydrotalcite, 15-25 pts. wt. diluent, 8-16 pts. wt. curing agent, 3-7 pts. wt. dispersant, 3-5 pts. wt. defoamer and 3-5 pts. wt. coupling agent. USE - Used as modified graphene aqueous anti-corrosion coating. ADVANTAGE - The coating: has excellent corrosion performance and mechanical property. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing modified graphene aqueous anti-corrosion coating comprising placing aqueous epoxy resin, octadecyl amine and silane co-modified graphene oxide, silane- modified zinc-copper-iron hydrotalcite and diluent into a high-speed mixer and mixing, where the stirring speed is 3000-4000 revolutions/minute, stirring for 20-60 minutes, adding curing agent, dispersant, defoamer and coupling agent to the above mixture and continuing stirring for 20-40 minutes to obtain anti-corrosion coating.