▎ 摘　　要

NOVELTY - High and low temperature heat conduction rubber material comprises e.g. 60-80 pts. wt. fluorine rubber, 20-40 pts. wt. silicone rubber, 30-50 pts. wt. fumed silica, 3-5 pts. wt. modified graphene, 20-40 pts. wt. magnesium hydroxide nanoparticles, 6-10 pts. wt. melamine phosphate, 10-15 pts. wt. methylphosphonate, 15-25 pts. wt. epoxidized soybean oil, 15-25 pts. wt. silkworm pupa epoxy butyl oleate, 0.8-1.2 pts. wt. peroxide di-iso-phenylpropyl, 1-3 pts. wt. triallyl cyanurate, 0.5-0.9 pts. wt. accelerant DM, 3-4 pts. wt. calcium/zinc composite stabilizer and 1-2 pts. wt. stearic acid filing. USE - Used as high and low temperature heat conduction rubber material. ADVANTAGE - The rubber material has good mechanical properties, high tensile strength and is tear resistance. DETAILED DESCRIPTION - High and low temperature heat conduction rubber material comprises 60-80 pts. wt. fluorine rubber, 20-40 pts. wt. silicone rubber, 30-50 pts. wt. fumed silica, 3-5 pts. wt. modified graphene, 20-40 pts. wt. magnesium hydroxide nanoparticles, 6-10 pts. wt. melamine phosphate, 10-15 pts. wt. methylphosphonate, 15-25 pts. wt. epoxidized soybean oil, 15-25 pts. wt. silkworm pupa epoxy butyl oleate, 0.8-1.2 pts. wt. peroxide di-iso-phenylpropyl, 1-3 pts. wt. triallyl cyanurate, 0.5-0.9 pts. wt. accelerant DM, 3-4 pts. wt. calcium/zinc composite stabilizer, 1-2 pts. wt. stearic acid filing, 1-3 pts. wt. antioxidant AW, 0.5-1.5 pts. wt. antioxidant D and 4-6 pts. wt. silicone powder.