  • 专利标题:   Preparation of high-strength wear-resistant and high-temperature resistant titanium aluminum alloy material, involves wet ball milling and mixing titanium aluminum pre-alloyed powder, graphene nanosheets and molybdenum to obtain mixed powder, pressing mixed powder into blank, and sintering.
  • 专利号:   CN113020604-A
  • 发明人:   ZHANG C, CUI X, ZHU W, MA C, HE X
  • 专利权人:   UNIV XIAN ARCHITECTURE TECHNOLOGY
  • 国际专利分类:   B22F003/16, B22F009/04, C22C001/05, C22C001/10, C22C014/00
  • 专利详细信息:   CN113020604-A 25 Jun 2021 B22F-009/04 202163 Pages: 7 Chinese
  • 申请详细信息:   CN113020604-A CN10246959 05 Mar 2021
  • 优先权号:   CN10246959

▎ 摘　　要

NOVELTY - The preparation of high-strength wear-resistant and high-temperature resistant titanium aluminum alloy material, involves wet ball milling and mixing titanium aluminum 4822 pre-alloyed powder, graphene nanosheets and molybdenum to obtain a mixed powder, pressing the mixed powder into a blank, vacuum hot pressing and sintering. USE - Preparation of high-strength wear-resistant and high-temperature resistant titanium aluminum alloy material (claimed). ADVANTAGE - The method enables preparation of high-strength wear-resistant high-temperature titanium oxide aluminum alloy material by simple process.