• 专利标题:   Graphene loading nano zinc oxide/silver complex material comprises graphene as a carrier and nano zinc oxide/silver complex graphene grown on surface or graphene nano zinc oxide/silver complex forming a package structure.
  • 专利号:   CN105498689-A, CN105498689-B
  • 发明人:   LI Z, MENG Y, WANG Y, WU H
  • 专利权人:   TANGSHAN JIDONG GRAPHENE TECHNOLOGY DEV CO LTD, TANGSHAN JIDONG GRAPHENE TECHNOLOGY DEV
  • 国际专利分类:   A01N059/16, A01P001/00, A01P003/00, B01D053/72, B01D053/86, B01J020/20, B01J020/28, B01J023/66
  • 专利详细信息:   CN105498689-A 20 Apr 2016 B01J-020/20 201646 Pages: 5 English
  • 申请详细信息:   CN105498689-A CN10900300 09 Dec 2015
  • 优先权号:   CN10900300

▎ 摘  要

NOVELTY - Graphene loading nano zinc oxide/silver complex material comprises graphene as a carrier and nano zinc oxide/silver complex graphene grown on surface or graphene nano zinc oxide/silver complex forming a package structure. USE - Used as graphene loading nano zinc oxide/silver complex material. ADVANTAGE - The material is simple to prepare, easy to control, stable with uniform size, removes indoor formaldehyde and has antibacterial and antifungal activity. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing graphene loading nano zinc oxide/silver complex material, comprising: (i) mixing zinc dust, silver nitrate solution and graphene oxide aqueous solution in the ratio 1.2-6:0.06-3:1, stirring at room temperature for 30 minutes, where the stirring speed is not less than 100 rotations/minute, sonicating for 30 minutes or more, stirring for 30 minutes for uniform mixing; (ii) placing the step (i) mixed solution in reaction vessel, carrying out temperature hydrothermal reaction at 130-200 degrees C for 1-6 hours; (iii) cooling the step (ii) reaction mixture, filtering, separating solid-liquid by centrifugation, drying the separated solid to obtain graphene supported nano zinc oxide/silver complex material precursor; and (iv) calcinating the step (iii) resultant to obtain the product.