• 专利标题:   Preparing ceramic slurry involves taking pretreated kaolin powder, flaky graphene oxide, coco fiber, anorthite powder, clay, pretreated quartz powder, urea, calcium nitrate solution, N'-hexadecyl-N,N-dimethylethyl hydrazine solution.
  • 专利号:   CN108383492-A
  • 发明人:   LEI G, YIN L, HUANG H
  • 专利权人:   JIANGSU XINYIYUAN ENVIRONMENTAL PROTECTION TECHNOLOGY CO LTD
  • 国际专利分类:   C04B033/13, C08G008/28, C08G008/20
  • 专利详细信息:   CN108383492-A 10 Aug 2018 C04B-033/13 201861 Pages: 10 Chinese
  • 申请详细信息:   CN108383492-A CN10199095 12 Mar 2018
  • 优先权号:   CN10199095

▎ 摘  要

NOVELTY - Preparing ceramic slurry involves taking 20-30 pts. wt. pretreated kaolin powder, 10-20 pts. wt. flaky graphene oxide, 20-30 pts. wt. coco fiber, 20-30 pts. wt. anorthite powder, 40-50 pts. wt. clay, 20-30 pts. wt. pretreated quartz powder, 8-10 pts. wt. urea, 8-10 pts. wt. calcium nitrate solution, 10-20 pts. wt. N'-hexadecyl-N,N-dimethylethyl hydrazine solution, 10-20 pts. wt. hexadecane, 10-20 pts. wt. plant essential oil, 20-30 pts. wt. modifying auxiliary agent, 60-80 pts. wt. Bacillus liquid mixed under constant temperature, and treating mixture once, mixing alkaline phenolic resin with the primary treatment mixture at a mass ratio of 1:10-1:20 to obtain a secondary treatment mixture. Argon gas is introduced into the secondary treatment mixture, and the mixture is heated and stirred to obtain a ceramic slurry. USE - Method for preparing ceramic slurry. ADVANTAGE - The method enables to prepare ceramic slurry which has excellent plasticity and water erosion resistance.