• 专利标题:   Graphene-organosilicon modified polyurethane aqueous coating for protection of cement concrete, metal and wood, comprises water-based urethane resin modified with graphene-organosilicon, leveling agent, dispersant and antifoaming agent.
  • 专利号:   CN106590399-A
  • 发明人:   KANG L
  • 专利权人:   KANG L
  • 国际专利分类:   C09D175/08, C09D005/08, C09D005/24, C09D007/12
  • 专利详细信息:   CN106590399-A 26 Apr 2017 C09D-175/08 201741 Pages: 6 Chinese
  • 申请详细信息:   CN106590399-A CN11262880 30 Dec 2016
  • 优先权号:   CN11262880

▎ 摘  要

NOVELTY - Graphene-organosilicon modified polyurethane aqueous coating comprises 38-80 pts. wt. water-based urethane resin modified with graphene-organosilicon, 3-8 portions propylene glycol monobutyl ether, 0.5-1.5 pts. wt. leveling agent, 0.5-1 pts. wt. water repellent, 0.5-1 pts. wt. dispersant, 0.5-1 pts. wt. antifoaming agent, 0.2-0.6 pts. wt. wetting agent and 10-30 pts. wt. deionized water. The graphene-organosilicon-modified aqueous polyurethane resin is obtained from polyisocyanate, polyhydric alcohols, polyamine chain extenders, oligomeric polyols, dimethylol propionic acid and silicone. USE - Graphene-organosilicon modified polyurethane aqueous coating used for protection of cement concrete, metal, wood and other structures. ADVANTAGE - The graphene-organosilicon modified polyurethane aqueous coating has a high cross-linking density, high hardness, good mechanical performance, good waterproof performance, corrosion resistance, antistatic property, high temperature resistance, aging resistance and chemical resistance. DETAILED DESCRIPTION - Graphene-organosilicon modified polyurethane aqueous coating comprises 38-80 pts. wt. water-based urethane resin modified with graphene-organosilicon, 3-8 portions propylene glycol monobutyl ether, 0.5-1.5 pts. wt. leveling agent, 0.5-1 pts. wt. water repellent, 0.5-1 pts. wt. dispersant, 0.5-1 pts. wt. antifoaming agent, 0.2-0.6 pts. wt. wetting agent and 10-30 pts. wt. deionized water. The graphene-organosilicon-modified aqueous polyurethane resin is obtained from polyisocyanate, polyhydric alcohols, polyamine chain extenders, oligomeric polyols, dimethylol propionic acid, silicone, graphene, neutralizing agent, deionized water through the chemical reaction in the system.