▎ 摘　　要

NOVELTY - Armor plate with a continuous gradient enhanced phase preparation involves mixing ethyl alcohol solution and graphene. The obtained 0.5-5 wt.% mixed solution is oscillated. The obtained oscillated mixture is added with ceramic powder. The obtained mixture is ground in a ball mill for 20-40 hours. The obtained mixture is dried in a drying box. The obtained drying product is injected in a molding device. The obtained mold is heated at 500-550 degrees C in presence of inert gas protection. The obtained product is heated in a crucible at 400-500 degrees C. The obtained heated product is preserved at 700-750 degrees C. USE - Method for preparing armor plate with a continuous gradient enhanced phase (claimed). ADVANTAGE - The method enables to prepare armor plate with a continuous gradient enhanced phase in an easy manner, and has high strength. DETAILED DESCRIPTION - Armor plate with a continuous gradient enhanced phase preparation involves mixing ethyl alcohol solution and graphene. The obtained 0.5-5 wt.% mixed solution is oscillated. The obtained oscillated mixture is added with ceramic powder. The obtained mixture is ground in a ball mill for 20-40 hours. The obtained mixture is dried in a drying box. The obtained drying product is injected in a molding device. The obtained mold is heated at 500-550 degrees C in presence of inert gas protection. The obtained product is heated in a crucible at 400-500 degrees C. The obtained heated product is preserved at 700-750 degrees C. The obtained product is cooled. The obtained cooled product is extruded at 400-450 degrees C.