• 专利标题:   Preparation of flaky agglomerated small spherical nano tungsten trioxide powder for photocatalytic process, involves mixing ammonium metatungstate and graphene oxide solution, freezing, freeze-drying, heat-preserving and calcining.
  • 专利号:   CN108862390-A
  • 发明人:   WEI S, PAN K, ZHAO Y, ZHANG C, MAO F, CHEN C, XU L, ZHOU Y, LI X, WANG F, YANG Y, WANG C
  • 专利权人:   UNIV HENAN SCI TECHNOLOGY
  • 国际专利分类:   C01G041/02, B82Y030/00, B01J023/30, C02F001/30
  • 专利详细信息:   CN108862390-A 23 Nov 2018 C01G-041/02 201906 Pages: 10 Chinese
  • 申请详细信息:   CN108862390-A CN10784321 17 Jul 2018
  • 优先权号:   CN10784321

▎ 摘  要

NOVELTY - Preparation of flaky agglomerated small spherical nano tungsten trioxide powder, involves (S1) separately stirring and mixing ammonium metatungstate and graphene oxide solution in a mass ratio of (60-600):1, preparing mixed raw material liquid, (S2) placing mixed raw material liquid under vacuum for 2-12 hours, taking out, freezing with liquid nitrogen, transferring to refrigerator at a temperature of -2-20 degrees C for 2-24 hours, preparing solid mixture, (S3) putting the solid mixture in freeze dryer, controlling the temperature at less than or equal to -60 degrees C, freeze-drying for 2-12 hours under vacuum degree of less than or equal to 10 Pa, preparing dry mixture, (S4) putting the dry mixture in muffle furnace, controlling the temperature in furnace at 350-850 degrees C, heat-preserving and calcining for 1-2 hours. USE - Preparation of flaky agglomerated small spherical nano tungsten trioxide powder for photocatalytic process. ADVANTAGE - The method enables simple and controllable preparation of flaky agglomerated small spherical nano tungsten trioxide powder with unique shape, uniform particle size, stability and excellent photocatalytic performance.