▎ 摘　　要

NOVELTY - Processing fabric involves dispersing graphene oxide in formamide solution to obtain dispersion with concentration of 0.3-0.5mg/mL. The ferric nitrate and nickel nitrate are dissolved in the dispersion and mixed uniformly to obtain mixed solution. The sodium hydroxide solution is slowly dropped and continuously reacted for 5-6 hours. The reaction is stopped when the pH is 10-10.5, continuously stirred for 1-2 hours, allowed to stand for 4-6 hours, collected precipitate, washed with absolute ethyl alcohol and deionized water alternately for 3-4 times, and dried to obtain modified hydrotalcite-type nanosheet compound. USE - The method is useful for processing fabric. ADVANTAGE - The surface of the fabric is formed with a composite layer for reducing friction; it can effectively reduce the friction of the fabric in the washing process, so as to reduce the abrasion of the fabric surface and improve the clothes performance of the fabric.