▎ 摘　　要

NOVELTY - Recycling waste porcelain comprises mixing and reacting ceramic slurry, graphene oxide and acid solution, and calcining at 1000-1200℃ and at reducing atmosphere, where the mass ratio of the ceramic slurry and graphene oxide is 5-6:1, the ceramic slurry comprises 100 pts. wt. waste porcelain, 70-80 pts. wt. kaolin, 25-30 pts. wt. bentonite and 20-25 pts. wt. ethyl orthosilicate. USE - The method is useful for recycling waste porcelain used as building filler, and as common road building filler, and light building material. ADVANTAGE - The method: fixes other preparation raw materials by ethyl orthosilicate; utilizes reducing atmosphere to reduce the graphene oxide to graphene; and improves the strength of the ceramic material.