• 专利标题:   Root-resistance environmentally friendly polymer cement waterproof coating used for waterproof construction of planting surface, comprises two components with preset weight mixing ratio.
  • 专利号:   CN115044260-A
  • 发明人:   LI Y, HUANG J, LIU G, WANG J
  • 专利权人:   YUNNAN XINCHENG WATERPROOF TECHNOLOGY CO
  • 国际专利分类:   C09D001/08, C09D125/14, C09D133/00, C09D005/08, C09D005/29, C09D005/32, C09D007/63, C09D007/65
  • 专利详细信息:   CN115044260-A 13 Sep 2022 C09D-133/00 202295 Chinese
  • 申请详细信息:   CN115044260-A CN10734981 27 Jun 2022
  • 优先权号:   CN10734981

▎ 摘  要

NOVELTY - Root-resistance environmentally friendly polymer cement waterproof coating comprises component A and component B, where the weight mixing ratio of component A to component B is 1:1-1:1.3. USE - The coating is useful for waterproof construction of planting surface in toilet bathing room, kitchen, building outer wall, waterproof construction of underground engineering and impounding reservoir. ADVANTAGE - The coating has good root resistance, environmental protection, high strength, high extension and strong base bonding. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for preparing root-resistance environmentally friendly polymer cement waterproof coating, comprising (1) preparing component A: component A is an aqueous solution, adding high molecular polymer emulsion, root inhibitor, surfactant, anti-foaming agent, preservative, dispersant, plasticizer, thickener, anti-aging agent, high-efficiency nano-adhesive and water, stirring and mixing to obtain product, (2) preparing Component B: component B is powder, sequentially adding cement, heavy calcium carbonate, quartz powder, kaolin, precipitated barium sulfate, mica powder and graphene powder, mixing, and stirring for 2 hours at medium speed, and (3) mixing: firstly placing component A into mixing, stirrer weighing a certain weight B component according to the mixing proportion, slowly pouring the component B into component A, stirring at a speed of 600 revolutions/minute for 10-15 minutes, reducing the speed to 300 revolutions/minute, and stirring for 5-10 minutes until there are no obvious bubbles in the coating.