• 专利标题:   Preparing graphene oxide-tannic acid/aqueous epoxy composite paint, comprises e.g. preparing graphene oxide-tannic acid dispersing solution, mixing with base material, then sand blasting high pressure spraying surface, and curing.
  • 专利号:   CN108587401-A
  • 发明人:   HE Y, CHEN C, WU Y, ZHONG F, QING D, LI H, XIA Y, LI J
  • 专利权人:   UNIV SOUTHWEST PETROLEUM
  • 国际专利分类:   C09D163/00, C09D005/08, C09D007/62
  • 专利详细信息:   CN108587401-A 28 Sep 2018 C09D-163/00 201875 Pages: 9 Chinese
  • 申请详细信息:   CN108587401-A CN10433480 08 May 2018
  • 优先权号:   CN10433480

▎ 摘  要

NOVELTY - Preparing graphene oxide-tannic acid/aqueous epoxy composite paint, comprises (1) adding 100 ml deionized water and 0.05 g tannic acid into a 250 ml beaker, and ultrasonic oscillating for 20 minutes to obtain a tannic acid solution, adding 0.1 g graphene oxide under ultrasonic oscillating condition (600 W), then dispersing in the tannic acid solution for 1 hour to obtain tannic acid intercalated graphene dispersion, then removing unreacted graphene oxide and tannic acid in the mixed solution through high speed centrifuge (speed of 1000-1500 revolutions/minute) to obtain a graphene oxide-tannic acid dispersing solution, and (2) mixing base material with the graphene oxide-tannic acid dispersing solution under stirring condition to form uniformly dispersed system, transferring the uniformly dispersed system into a spray gun, sand blasting high pressure spraying surface by a rectangular steel sheet, curing at room temperature for 2 days. USE - The method is useful for preparing graphene oxide-tannic acid/aqueous epoxy composite paint. ADVANTAGE - The graphene oxide-tannic acid/aqueous epoxy composite paint has improved anticorrosive ability. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for graphene oxide-tannic acid/aqueous epoxy composite paint obtained by above mention method.