▎ 摘　　要

NOVELTY - A nickel-aluminum alloy material comprises 6-10 wt.% silicon, 1-3.5 wt.% magnesium, 0.15-0.85 wt.% iron, 0.5-1.5 wt.% chromium, 1.2-2.6 wt.% zinc, 0.01-0.08 wt.% boron, 3-8 wt.% graphene oxide, 6-20 wt.% nickel, and balance aluminum. USE - Nickel-aluminum alloy material. ADVANTAGE - The material is a three-dimensional network structure and has good stretchability and flexibility, improved compatibility, enhanced adhesion capability, and improved overall performance. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for preparation of material comprising taking graphene powder and weighing; weighing raw materials and milling until particle diameter is less than 0.01 mu m; stirring, placing into graphitization furnace, heating to 50-80 degrees C, heating to 150-300 degrees C under inert gas protection, where heating rate is 10-25 degrees C/minute, melting, adding to graphene powder, stirring, and cold forming.