• 专利标题:   Making titanium dioxide/chitosan/graphene oxide composite material involves dispersing graphene oxide into dilute acetic acid, adding chitosan powder and titanium dioxide, dripping glue liquid into sodium hydroxide solution, washing, drying.
  • 专利号:   CN103521191-A, CN103521191-B
  • 发明人:   CHENG Y, HE H, LUO S, YANG C, ZENG G, TU Y
  • 专利权人:   UNIV HUNAN
  • 国际专利分类:   B01J020/24, B01J020/28, B01J020/30, C02F001/28, C02F001/62
  • 专利详细信息:   CN103521191-A 22 Jan 2014 B01J-020/24 201421 Pages: 8 Chinese
  • 申请详细信息:   CN103521191-A CN10480329 15 Oct 2013
  • 优先权号:   CN10480329

▎ 摘  要

NOVELTY - Preparing titanium dioxide/chitosan/graphene oxide composite material involves dispersing 0.05-1 g graphite oxide into 50 ml volume fraction of 5-8% dilute acetic acid at normal temperature, adding chitosan powder, continuously stirring for 3-5 hours, slowly adding titanium dioxide at 40-60 degrees C at constant temperature, continuously stirring and reacting for 3 hours to form glue solution, dripping the glue solution into 0.1 M sodium hydroxide solution, standing for 4-12 hours, washing to neutral, freezing and drying to obtain the composite material. USE - For preparing titanium dioxide/chitosan/graphene oxide composite material which is useful for processing waste water containing heavy metal arsenic (claimed). ADVANTAGE - The method is simple and environment-friendly; and has high efficiency.