• 专利标题:   Preparation of copper-nickel double-metal nitrogen-carbon material for carbon dioxide electrochemical reduction, involves putting urea in crucible, transferring to muffle furnace for calcining, and adding ammonia water for hydrothermal reaction.
  • 专利号:   CN115094442-A
  • 发明人:   XU N, LI L, HE R, XU B, QIAO J
  • 专利权人:   UNIV DONGHUA
  • 国际专利分类:   C25B001/23, C25B011/069, C25B011/091
  • 专利详细信息:   CN115094442-A 23 Sep 2022 C25B-001/23 202202 Chinese
  • 申请详细信息:   CN115094442-A CN10492771 07 May 2022
  • 优先权号:   CN10492771

▎ 摘  要

NOVELTY - Preparing copper nickel double metal nitrogen carbon material comprises (i) placing urea in a crucible, transferring to a muffle furnace for calcination; (ii) placing carbon nitride and graphene oxide in a reactor, and introducing aqueous ammonia to carry out hydrothermal reaction; (iii) powder after step 2) after the reaction is suction filtered and dried to obtain base material; (iv) base material obtained in step 3) and copper phthalocyanine, nickel phthalocyanine and methanol are placed in an alumina ball mill tank and transferred to a planetary ball mill for ball milling; (v) vacuum-dry the solution after ball milling; (vi) placing dried powder in an alumina crucible, transfering to a tube furnace, and heat-treating under a nitrogen atmosphere, and cooling to room temperature. USE - The method is useful for preparing copper-nickel double-metal nitrogen-carbon material, which is useful in carbon dioxide electrochemical reduction. ADVANTAGE - The method is simple and economic, easy to operate, and provides copper-nickel double-metal nitrogen carbon material with improved conductivity and stability, and improved catalytic reduction performance. The metal phthalocyanine has low cost, excellent electronic characteristics.