• 专利标题:   Anti-corrosion material comprises epoxy resin, alkyd resin, phenolic resin, silicone oil, graphene, leveling agent, curing agent and filler.
  • 专利号:   CN106590372-A
  • 发明人:   FU Z
  • 专利权人:   TIANJIN ANNAN TECHNOLOGY CO LTD
  • 国际专利分类:   C09D161/06, C09D163/00, C09D167/08, C09D183/04, C09D005/08, C09D007/12
  • 专利详细信息:   CN106590372-A 26 Apr 2017 C09D-167/08 201735 Pages: 6 Chinese
  • 申请详细信息:   CN106590372-A CN11126616 09 Dec 2016
  • 优先权号:   CN11126616

▎ 摘  要

NOVELTY - Anti-corrosion material comprises 80-200 pts. wt. epoxy resin, 100-220 pts. wt. alkyd resin, 20-30 pts. wt. phenolic resin, 20-30 pts. wt. silicone oil, 3-8 pts. wt. graphene, 10-20 pts. wt. leveling agent, 3-8 pts. wt. curing agent and 30-80 pts. wt. filler. USE - Used as anti-corrosion material. ADVANTAGE - The material has self-cleaning function, strong anti-corrosion properties in an extreme environment e.g. moisture, acid and alkali for long time, and long service life, and can be easily cured at normal temperature. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing anti-corrosion material comprising (i) adding 80-200 pts. wt. epoxy resin, 100-220 pts. wt. alkyd resin, 20-30 pts. wt. phenolic resin, 20-30 pts. wt. silicone oil into the stirred tank at room temperature, mixing for 4-10 minutes, (ii) heating at 45-60 degrees C, adding 3-8 pts. wt. graphene, 10-20 pts. wt. leveling agent and 30-80 pts. wt. filler, stirring for 4-10 minutes, and (iii) cooling to 0-4 degrees C, adding -8 pts. wt. curing agent, continuously stirring for 4-10 minutes, then storing at 0-8 degrees C low temperature to obtain final product.