▎ 摘　　要

NOVELTY - A modified carbon fiber-doped graphene-based aerogel electrode material comprises 3-6 pts. wt. carbon fiber, 10-20 pts. wt. graphene, 10-20 pts. wt. glucose, 10-20 pts. wt. dimethylformamide, 20-30 pts. wt. zinc chloride solution having concentration of 2-5 mol/l, 5-10 pts. wt. isophorone diisocyanate, 30-40 pts. wt. potassium permanganate, 80-100 pts. wt. ethanol, appropriate amount of chloroform, 3-5 pts. wt. silane coupling agent KH56, 20-30 pts. wt. pyrrole, 35-45 pts. wt. p-toluenesulfonic acid, 35-40 pts. wt. ammonium persulfate solution and 500-1000 pts. wt. distilled water. USE - Modified carbon fiber-doped graphene-based aerogel electrode material for use in supercapacitor. ADVANTAGE - The modified carbon fiber-doped graphene-based aerogel electrode material has increased the specific capacitance of super capacitor, improved conductivity and improved cycle performance. DETAILED DESCRIPTION - A modified carbon fiber-doped graphene-based aerogel electrode material comprises 3-6 pts. wt. carbon fiber, 10-20 pts. wt. graphene, 10-20 pts. wt. glucose, 10-20 pts. wt. dimethylformamide, 20-30 pts. wt. zinc chloride solution having concentration of 2-5 mol/l, 5-10 pts. wt. isophorone diisocyanate, 30-40 pts. wt. potassium permanganate, 80-100 pts. wt. ethanol, appropriate amount of chloroform, 3-5 pts. wt. silane coupling agent KH56, 20-30 pts. wt. pyrrole, 35-45 pts. wt. p-toluenesulfonic acid, 35-40 pts. wt. ammonium persulfate solution having concentration of 3-6 mol/l and 500-1000 pts. wt. distilled water. An INDEPENDENT CLAIM is also included for a method for preparing a modified carbon fiber-doped graphene-based aerogel electrode material.