• 专利标题:   Preparation of high tensile strength graphene-diazo resin crosslinked composite material includes adding graphene oxide to deionized water, performing ultrasonication to obtain uniform dispersion of graphite oxide and adding diazo resin.
  • 专利号:   CN104072944-A, CN104072944-B
  • 发明人:   CHEN X, WANG Y
  • 专利权人:   UNIV BEIJING AERONAUTICS ASTRONAUTICS, UNIV BEIHANG
  • 国际专利分类:   C08J003/28, C08J005/18, C08K003/04, C08L061/22
  • 专利详细信息:   CN104072944-A 01 Oct 2014 C08L-061/22 201501 Pages: 11 Chinese
  • 申请详细信息:   CN104072944-A CN10314516 03 Jul 2014
  • 优先权号:   CN10314516

▎ 摘  要

NOVELTY - Preparation of high tensile strength graphene-diazo resin crosslinked composite material involves adding graphene oxide to deionized water, performing ultrasonication to obtain uniform dispersion of graphite oxide, adding 0.1-2 mL diazo resin at room temperature in dark room, stirring for 2-12 hours, performing vacuum filtering using anodized aluminum filter film, drying, peeling off composite film from membrane, performing UV light irradiation for 120-300 seconds, placing in hydrogen iodide solution at 100 degrees C for 1-2 hours, cooling and drying. USE - Method for preparing high tensile strength graphene-diazo resin crosslinked composite material (claimed). ADVANTAGE - The method is simple and easy to operate. The crosslinked composite material has excellent mechanical property and conductivity.