• 专利标题:   Preparing spherical shell-shaped three-dimensional graphene comprises e.g. uniformly mixing copper(ii) sulfate and nickel(ii) sulfate, washing, heating under vacuum, carrying out reduction treatment and graphene deposition process.
  • 专利号:   CN105417527-A, CN105417527-B
  • 发明人:   GUO X, JIANG J, ZENG Y, ZHANG X, HE M, CHEN J, GE C, LI C
  • 专利权人:   UNIV SOUTHEAST
  • 国际专利分类:   B82Y040/00, C01B031/04, C01B032/186
  • 专利详细信息:   CN105417527-A 23 Mar 2016 C01B-031/04 201638 Pages: 7 English
  • 申请详细信息:   CN105417527-A CN10904410 09 Dec 2015
  • 优先权号:   CN10904410

▎ 摘  要

NOVELTY - Preparing spherical shell-shaped three-dimensional graphene comprises (i) uniformly mixing copper(ii) sulfate, nickel(ii) sulfate and sulfuric acid by transferring into a ball crystallization accelerator; (ii) washing the step (i) product reputedly with ultrapure water, filtering and freeze drying; and (iii) placing the lyophilized sample in a vacuum oven, carrying out first reduction treatment in a hydrogen atmosphere, carrying out graphene deposition process at a high temperature in a mixed atmosphere of hydrogen and methane and removing metal substrate. USE - The method is useful for preparing spherical shell-shaped three-dimensional graphene (claimed). ADVANTAGE - The method has simple operation. The product has good catalyzing effect. DETAILED DESCRIPTION - Preparing spherical shell-shaped three-dimensional graphene comprises (i) uniformly mixing copper(ii) sulfate, nickel(ii) sulfate and sulfuric acid by transferring into a ball crystallization accelerator, depositing the mixed solution on the copper sheet working electrode, where the sheet comprises copper or copper-nickel cluster, to obtain mixed solution deposited on the sheet; (ii) washing the step (i) product reputedly with ultrapure water, filtering and freeze drying; and (iii) placing the lyophilized sample in a vacuum oven, carrying out first reduction treatment in a hydrogen atmosphere, carrying out graphene deposition process at a high temperature in a mixed atmosphere of hydrogen and methane and removing metal substrate using ammonium persulfate solution or ferric trichloride solution, to obtain the final product.