▎ 摘　　要

NOVELTY - Manufacture of positive electrode sheet involves heating graphite oxide to 900-1200 degrees C for 30-150 seconds under anaerobic conditions, forming graphene, mixing graphene, adhesive agent, conductive agent and N-methyl pyrrolidone, forming mixed slurry, coating mixed slurry on positive electrode collector, drying, coating organolithium compound solution on electrode film, heating at 50-70 degrees C for 1-3 hours and 100-120 degrees C for 12-36 hours under anaerobic condition, cold-rolling, and trimming. USE - Manufacture of positive electrode sheet used for manufacturing lithium-ion capacitor (claimed). ADVANTAGE - The positive electrode sheet is manufactured efficiently by simple method. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for manufacture of lithium-ion capacitor.