• 专利标题:   Preparing conductive and thermally conductive graphite film comprises e.g. mixing weakly oxidized graphite without metal ion and graphene oxide aqueous solution, suction filtering mixed solution, drying and pressing to obtain composite film and subjecting to high-temperature graphitization treatment.
  • 专利号:   CN115818635-A
  • 发明人:   CHEN N, LUO Y, GANG Z, CHEN F, SHEN P
  • 专利权人:   UNIV SICHUAN
  • 国际专利分类:   C01B032/205, C01B032/225
  • 专利详细信息:   CN115818635-A 21 Mar 2023 C01B-032/205 202332 Chinese
  • 申请详细信息:   CN115818635-A CN11598739 14 Dec 2022
  • 优先权号:   CN11598739

▎ 摘  要

NOVELTY - Preparing conductive and thermally conductive graphite film comprises (a) intercalating graphite under the action of expansion agent and sulfuric acid, the gas generated by the decomposition of the expansion agent in sulfuric acid causes the graphite to expand and form expanded graphite, stripping the expanded graphite to obtain weakly oxidized graphite without metal ions, where the expansion agent is persulfide, (b) uniformly mixing weakly oxidized graphite without metal ion and graphene oxide aqueous solution in a mass ratio of 100:2-20 to obtain a mixed solution, performing suction filtration on the mixed solution to obtain a product, and (c) drying and pressing the obtained product to obtain weakly oxidized graphite/graphene oxide composite film, subjecting the obtained weakly oxidized graphite/graphene oxide composite film to high-temperature graphitization treatment. USE - Preparation method of conductive and thermally conductive graphite film is useful ffor electronic equipment i.e. desktop computer, notebook computer, smart mobile phone, etc. ADVANTAGE - The graphite film has good mechanical property, high thickness, high conductivity, tensile strength, and electromagnetic shielding performance of the lifting. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for conductive and thermally conductive graphite film prepared by the above-mentioned method.